RE:RE:RE:RE:RE:RE:RE:RE:RE:RE:RE:RE:RE:RE:RE:Kozmo Truce with answers Hi Kozmo, on standalone figures I a hard rock deposit I would agree with you but I have looked at the work done and I can see where the development team are going with the method they are proposing and scientifically it's very possible.
1. Extract the material with the same SG - Tin, Tantalum
2. by definition this would leave you with an concentrated waste pile of Li and SiO2.
3. Process the higher grade Li waste pile (almost like preconcentration)
if and I say if this works it will be a process considered before but never used because you would need a lot of volume and that's where the 105Mio tons comes in at low cost (no mining cost and no strip ratio)
glad we can talk it through though and I'm not putting in false hope in anyone. I truly believe, hence why I invested, that if they go this route they can do it. If they drill the area South West as well (it is a prominent area this we can't deny as the aeromag Features are pretty clear with the high K anomalies like that of Richie Dure).